Machine and method for forming articles

ABSTRACT

A machine and method of forming an article generally comprising extruding a molten bead of thermoplastic material along x, y and z axes in forming an article consisting of a strata of such material, and passing a roller over each applied portion of such molten bead to compress such bead portion, enhancing the fusion of engaging plies of such extruded material.

BACKGROUND OF THE INVENTION

In the prior art, there has been developed a process generally referred to as an additive manufacturing process which generally consists of forming and extruding a bead of molten thermoplastic material, applying such bead of molten material in a strata of layers to form a facsimile of an article and then machining such facsimile to provide an end product. Typically, such thermoplastic material is infused with a type of reinforcing fiber to enhance its strength. As a general practice, the molten bead, while still hot and pliable, is tamped down using an oscillating plate to create a flattened layer of material of a specific desired thickness. This process is repeated so that each layer is deposited upon an existing layer to build up a structure. When executed properly, the new material being deposited is of a temperature sufficient enough to allow it to melt and fuse with material previously deposited, thus producing a solid part The tamping plate is generally configured as a flat plate with a center through-hole, situated concentric with the centerline of the extrusion nozzle, thus providing for effective tamping of the extruded material, regardless of the direction in which the head is moving. This tamping plate not only tamps and flattens the thermoplastic bead but also helps fuse it with the previously laid layer of material.

In the practice of the aforementioned process, several disadvantages have been encountered; most notably, air pockets, which are trapped between layers of thermoplastic material during the extrusion/deposition process, are simply tamped into the structure. In addition to creating problems during any temperature cycling that might occur after the part has cooled and hardened, such entrained air pockets invariably result in internal voids as well as surface imperfections in the final machined article. A further disadvantage of using a tamping plate is the insufficient integration of reinforcing fibers between layers. When two smooth beads of this material are forced together, the plastic component of the bead tends to fuse with the plastic component of the mating bead, with little or no reinforcing fibers crossing the area where the layers meet. Consequently, the joints between layers where there is no reinforcing material seriously affect the structural integrity of the overall article. Additionally, the mechanism employed to quickly oscillate the tamping plate is by necessity, quite complex, expensive and difficult to maintain.

In view of the forgoing, it is the principal object of the present invention to provide an improved method of producing articles through the use of an additive manufacturing process. Another object of the invention is to provide such a machine and method functional to provide more effective fusion of engaging plies of molten material. A still further objective of the invention is to provide such improved machine and method without the requirement of complex and expensive devices.

BRIEF DESCRIPTION OF THE INVENTION

The principal object of the present invention is achieved by means of a programmable CNC machine operable in forming an article supported on a work surface disposed in an x-y plane, either fixed or displaceable along an x-axis; an extruder disposed along an axis fixed or displaceable along an x-axis, displaceable along y and z axes, rotatable about its axis and pivotal about an x-axis; means for supplying a bead of molten plastic material through such extruder; means cooperable with either such work surface or a previously applied ply of such material for guiding and compressing a portion of such bead emanating from such extruder in forming an article consisting of stratified layers of such extruded material; a set of servomotors operable in displacing such components linearly, rotationally and/or pivotally and a suitably programmed computer for operating such motors. Such means for guiding and compressing a portion of such bead of molten material emanating from such extruder comprises a roller provided with an axis of rotation disposed along a line of intersecting of a first plane disposed perpendicular to the axis of the material emitting passageway of such extruder and a second plane disposed parallel to such passageway axis. Preferably, such bead of molten material is provided with reinforcing fibers interspersed therein which function to enhance the fusion of adjoining plies of such material, guided and compressed by such roller.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a CNC machine operable pursuant to an additive manufacturing process in forming articles, incorporating the present invention;

FIG. 2 is an enlarged perspective view of the carriage and applicator assembly of the machine shown in FIG. 1;

FIG. 3 is an enlarged perspective view of the, lower segment of the applicator assembly shown in FIG. 2;

FIG. 4a is an enlarged cross-sectional view of the material applicator head mounted on the lower end of the applicator assembly, illustrating the nozzle of a conduit for supplying a molten bead of thermoplastic material fully inserted into a passageway therethrough;

FIG. 4b is a view similar to the view of FIG. 4a , illustrating the nozzle thereof fully inserted into the passageway thereof;

FIG. 5 is a view similar to the view shown in FIG. 4a , illustrating a bead of molten material being extruded by the applicator bead shown in FIG. 4a onto a work surface, and a roller thereof engaging and compressing a portion of such bead against, such work surface, forming a ply of an article being formed;

FIG. 6a is an enlarged perspective view of the lower end of the assembly shown in FIG. 2, provided with a roller formed with transversely spaced grooves; and

FIG. 6b is a view similar to the view shown in FIG. 6a but with a roller formed with a transversely curved configuration.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT OF THE INVENTION

Referring to FIG. 1 of the drawings, there is illustrated a programmable computer numeric control (CNC) machine embodying the present invention which includes a bed 20 provided with a pair of transversely spaced side walls 21 and 22, a gantry 23 supported on side walls 21 and 22, carriage 24 mounted on gantry 23, a carrier 25 mounted on carriage 24 and an applicator assembly 26 mounted on carrier 25. Supported on bed 20 between side walls 21 and 22 is a worktable 27 provided with a support surface disposed in an x-y plane, which may be fixed or displaceable along an x-axis. In the displaceable version, the worktable is displaceable along a set of rails mounted on the bed by means of servomotors mounted on the bed and operatively connected to the worktable. Gantry 23 is disposed along a y-axis, supported at the ends thereof on end walls 21 and 22, either fixedly or displaceably along an x-axis on a set of guide rails 28 and 29 provided on the uppers ends of side walls 21 and 23. In the displaceable version, the gantry is displaceable by a set of servomotors mounted on the gantry and operatively connected to tracks provided on the side walls of the bed. Carriage 24 is supported on gantry 23 and is provided with a support member 30 mounted on and displaceable along a set of guide rails 31, 32 and 33 provided on the gantry. It is displaceable along a y-axis on such rails by a servomotor mounted on the gantry and operatively connected to support member 30. Carrier 25 is mounted on a set of spaced, vertically disposed guide rails 34 and 35 supported on the carriage for displacement of the carrier relative to the carriage along a z-axis. It is displaceable along such axis by a servomotor mounted on the carriage and operatively connected to the carrier.

As best shown in FIG. 2, carrier 25 is provided with a base platform 36, a gear box 37 fixedly mounted in the upper side thereof and a mounting platform 38 rotatably mounted on the underside thereof, provided with openings therethrough disposed along the z-axis of the carrier. Such gear box is provided with a gear arrangement provided with an opening therethrough disposed coaxially with the aligned openings in gear box 37 and platforms 36 and 38, operatively connected to platform 38 for rotation about such x-axis, and rotatable about such axis by means of a servomotor 39 mounted on base platform 36 and operatively connected to such gear arrangement.

Applicator assembly 26 includes an upper segment 41 and a lower segment 42. Segment 41 includes a transverse portion 41 a secured to the underside of mounting platform 38 for rotational movement about the z-axis, provided with an opening therethrough along such z-axis, and a depending portion 41 disposed laterally relative to such axis. Segment 42 consisting of a housing disposed on an inner side of depending segment portion 41 b, is mounted on a shaft journalled in a lower end of portion 41 b, intersecting and disposed perpendicular to the z-axis of carrier 25, and further is provided with a laterally projecting application head 43 at a free end thereof. Mounted on a bracket 44 provided on an outer side of segment portion 41 b is a servomotor 45 operatively connected to the shaft journalled in portion 41 b for pivotally displacing segment 42 in y-z plane.

Referring to FIGS. 4a and 4b , applicator head 43 includes a housing 46 mounted on and projecting laterally from the lower end of segment 42, and a bracket 47, Housing 46 is provided with a cylindrical opening 48 therethrough provided with an enlarged portion, a roller bearing 49 mounted in such enlarged portion of such opening and a cylindrical sleeve 50 disposed in such enlarged portion, mounted on the inner race of such bearing, having an inner diameter corresponding to opening 48 and including a portion extending beyond housing 46. Housing opening 48 and sleeve 50 are configured to receive therein a nozzle 51 of a flexible conduit 52 for conveying and extruding a molten bead 53 of a thermoplastic material through such nozzle provided with an output die 54 as shown in FIG. 5.

Bracket 47 includes an annular base portion 55 coaxially mounted on the lower, exposed end of sleeve 50 and rotatable with sleeve 50 about the axis thereof, an annular plate portion 56 coaxially mounted on annular base portion 55 and spaced axially relative to bearing 49, and a sprocket 56 a mounted on base portion 55, coaxially on exposed portion 55. Bracket 47 further includes a pair of spaced depending brackets 57, 57 supporting a shaft 58 on which there is mounted a rotatable roller 59, The axis of rotation of shaft 58 is disposed along the line of intersection of a first plane disposed perpendicular to the axis of passageway 48 and a second plane disposed parallel to such axis.

As best shown in FIG. 3, bracket 47 is rotatably displaceable about the axis thereof by a servomotor 60 supported on an L-shaped bracket 61 mounted on a lower rear side of lower applicator segment 42, having an output shaft 62 projecting through an opening 63 in bracket 61, provided with a sprocket 64 drivingly connected to sprocket 56 by means of a belt 65.

Conduit 52 consists of an elongated, flexible material for conducting a molten bead of a thermoplastic material under pressure from a source disposed on carrier 25 or another source, to applicator head 43. An intermediate portion of such conduit is routed through the openings through gear box 37, support platform 36 and mounting platform 38, along the z-axis of carrier 25. Such material is heated sufficiently to form a molten bead thereof, readily guide such bead through conduit 52 and extrude it through applicator head 43 in forming a strata of plies fusing together in forming an article. Such material supplied through such conduit and extruded to form an article may be provided with fibers which facilitate and enhance the fusion of extruded, engaging plies.

In the use of the machine as described in forming an article pursuant to the additive manufacturing method, with the machine suitably programmed and activated, a bead of molten material would be extruded along a defined path either on support surface 27 of the machine or previously extruder plies of such material, ahead of the path of roller 59, and caused to be engaged and compressed by such roller either against such support surface of a previously applied heated ply of material, fusing such plies together to form an object consisting of a strata of material plies fused together forming either an end product or an oversized, near duplicate thereof.

In the course of forming such article, the control system of the machine, in executing the, inputted program, would operate the several servomotors as described to displace the support surface or gantry along the x-axis, displace the carriage along the y-axis, displace the carrier along a z-axis, pivot lower applicator segment 42 about an axis disposed in an x-y plane and rotate bracket 47 about a z-axis thereof, pursuant to the inputted program, to provide the described end product or an oversized, near duplicate thereof.

The bead engaging portion of roller 59 may be cylindrical as shown in FIG. 5, serrated as shown in FIG. 6a or curved along the length thereof as shown in FIG. 6b . In circumstances where reinforcing fibers are provided in the molding material applied, it is preferred to utilize a roller with an irregular surface as shown in FIG. 6a which is effective in causing outlying portions of such fibers to engage and penetrate heated adjacent plies, enhancing the fusion of such plies.

In the practice of the invention as described, an article may be formed simply by forming a strata of plies defining the intended final configuration of the article; forming a strata of plies defining an interim configuration minimally exceeding the intended final configuration and then machining such interim configuration to provide the final configuration thereof; providing a permanent substructure preferably of a metal, having a configuration smaller than the intended final configuration of the article, and forming a strata of plies on such substructure providing the intended final configuration of the article; providing a permanent substructure preferably of a metal, having a configuration smaller than the intended final configuration of the article, forming a strata of plies on such substructure in forming an interim configuration slightly greater than the intended final configuration and then machining such interim configuration to provide the intended final configuration; providing a mold having a configuration smaller than the intended final configuration of the article, forming a strata of plies on such mold slightly greater than the intended final configuration of the article, machining such interim configuration to provide the final configuration of the article and then removing such mold; and providing a mold having a configuration smaller than the intended final configuration of the article, forming a strata of plies on such mold slightly greater than the intended final configuration of the article, machining such interim configuration to provide the final configuration of the article and then removing such mold.

From the foregoing detailed description, it will be evident that there are a number of changes, adaptations and modifications of the present invention, which come within the province of those persons having ordinary skill in the art to which the aforementioned invention pertains. However, it is intended that all such variations not departing from the spirit of the invention be considered as within the scope thereof as limited solely by the appended claims. 

1. A programmable CNC machine operable in producing an article of a selected configuration comprising: a worktable supported on a bed, laving a support surface disposed in an x-y plane, disposed in one of a fixed condition on said bed and a displaceable condition, along the y-axis; a gantry supported on said bed along an x-axis, disposed in one of a fixed condition on said bed with a worktable displaceable long the y-axis and a displaceable condition along the y-axis of said bed with said worktable disposed in a fixed condition; carriage mounted on said gantry, displaceble along the x-axis; a carrier mounted on said carriage, displaceable along a z-axis; an applicator assembly including an upper segment depending from said carrier and rotationally connected thereto about said z-axis, and a lower segment rotatably connected to said upper segment for pivotal movement relative to said upper segment about a pivotal axis intersecting said z-axis, provided with a cylindrical passageway therethrough provided with an axis disposed in an x-z plane; a conduit for conducting a bead of molten thermoplastic material, having an inlet connectable to a source of said material and an outlet inserted into said lower segment cylindrical passageway; a bracket mounted on an underside of said lower segment, rotatable about the axis of said lower segment passageway, having a passageway therethrough disposed coaxially with said lower segment passageway, and a roller depending therefrom provided with an axis disposed along the line of intersection of a first plane disposed perpendicular to said segment cylindrical passageway and a second plane disposed parallel to said segment cylindrical passageway; a plurality of servomotors each operatively connected to one of said aforementioned moveable components for selectively displacing said component one of a rotational and linear movement; and a computer functional pursuant to the execution of an inputted program for operatively controlling said servomotors.
 2. The machine according to claim 1 including means disposed on said carrier functional in holding a supply of a heated thermoplastic material and wherein said conduit is formed of a flexible material having an inlet for receiving a bead of said material from said holding means, an intermediate portion extending through passageways provided in said carrier and upper segment of said applicator assembly and an outlet received into and through said cylindrical passageway of said bracket for depositing a molten bead of said thermoplastic material onto a surface disposed ahead of a line of travel of said roller.
 3. The machine of claim 2 wherein the outlet of said cylindrical passageway of said bracket is functional to deposit an extruded portion of said molten bead on one of a work surface or a previously deposited molten bead, ahead of said roller which upon advancement thereof is functional in engaging and compressing extruded portions of said molten bead thereby compressing said extruded bead against a work surface or a previously extruded molten bead portion.
 4. The machine of claim 3 wherein the surface of the bead engaging portion of said roller is formed of a configuration functional upon pressing engagement with a bead of molten material extended through said bracket to enhance the juncture of mating plies of said extruded material.
 5. The machine of claim 3 wherein the molten bead engaging portion of said roller is provided with a set of spaced, annular grooves disposed concentric with the axis of rotation of said roller.
 6. The machine of claim 3 wherein the molten bead engaging portion of said roller is provided with a transversely curved configuration.
 7. The machine of claim 3 wherein the surface of the molten bead engaging portion of said roller is formed of a configuration, functional upon pressing engagement of a bead of molten material extruded through said bracket to be compressed and cause exposed portion of reinforcing fibers interspersed in said material to engage and become entrained in adjoining bead portions, improving the adhesion of adjoining bead portions.
 8. The machine of claim 1 wherein said bracket includes a sprocket disposed coaxially with said axis of such passageway therethrough, drivingly connected to an output shaft of a servomotor mounted on said lower segment of said applicator assembly.
 9. The machine of claim 1 including a bearing provided with an outer race mounted on said lower segment of said applicator assembly concentrically with the axis of said passageway therethrough and an inner race connected to said bracket.
 10. The machine of claim 1 wherein the axis of said roller is spaced from the axis of said passageway in said bracket sufficient to allow a bead of said molten thermoplastic material extruded through said passageway onto a support surface or a previously applied ply of said material to be engaged and compressed by the roller.
 11. The machine of claim 1 including a gear box mounted on said carrier drivable by a servomotor mounted on said carrier, and drivingly connected to said upper segment of said applicator assembly.
 12. The machine of claim 11 wherein said gear box, a portion of said carrier supporting said gear box and said upper segment of said applicator assembly are provided with a set of aligned passageways therethrough, and said bead conducting conduit extends therethrough.
 13. The machine of claim 1 wherein said upper segment of said applicator assembly is disposed in an x-y plane and said lower segment of said assembly projects downwardly from said upper segment spaced laterally of said z-axis.
 14. The machine of claim 13 including a shaft journalled in said lower segment of said applicator assembly, disposed in an x-y plane and intersecting said z-axis, an arm member mounted on said shaft, supporting said bracket thereon, and a servomotor mounted on said lower segment operatively connected to said shaft for pivotal displacement thereof about the axis of rotation thereof.
 15. A bracket mountable on and maneuverable by a machine for applying a bead of molten thermoplastic material onto one of a machine support surface and a previously applied ply of said material in the formation of an article comprising: a plate provided with a passageway along an axis therethrough for receiving and extruding a molten bead of said material therethrough onto one of said support surface and a previously applied ply of said material, when mounted on said machine; and a roller mounted on said plate having an axis of rotation spaced from said passageway axis sufficiently to allow a contact surface thereof to engage and receive a portion of said bead material extruded through said passageway and applied on one of said support surface and a previously applied ply of material, and compress said engaged bead portion in forming said object, wherein upon operatively mounting said bracket on said machine, said plate would be displaceable linearly along x, y and z axes, rotatably about an axis disposed in an x-y plane and rotatably about said passageway axis.
 16. The bracket of claim 15 wherein the surface of the bead engaging portion of said roller is formed of a configuration functional upon, pressing engagement of a bead of molten material extruded through said plate opening to enhance the juncture of mating plys of said extruded material.
 17. The bracket of claim 15 wherein the molten bead engaging portion of said roller is provided with a set of spaced, annular grooves disposed concentric with the axis rotation of said roller.
 18. The bracket of claim 15 wherein the molten bead engaging portion of said roller is provided with a transversely curved configuration.
 19. The bracket claim 15 wherein the surface of the molten bead engaging portion of said roller is formed of a configuration, functional upon pressing engagement of a bead of molten material extruded through said bracket to be compressed and cause exposed portions of reinforcing fibers interspersed in said material to engage and become entrained in adjoining bead portions, improving the adhesion of adjoining plies.
 20. The bracket of claim 15 including a sprocket disposed coaxially with said plate passageway, drivingly connectable to the output shaft of a servomotor.
 21. A method of forming an article on a work surface comprising: applying a bead of molten thermoplastic material on said work surface along a selected path including at least one ply functional to produce an object of a prescribed configuration; and guiding a roller over applied plies of said material in compressing relation to merge engaging plies together.
 22. The article formed in accordance with the method of
 21. 23. The method of claim 21 including integrating reinforcing fibers in said bead of material functional in enhancing the fusion of engaging plies.
 24. The article formed in accordance with the method of claim
 23. 25. The method of claim 21 including extruding said bead of material in the path of said roller immediately ahead thereof.
 26. The article formed in accordance with the method of claim
 25. 27. The method of claim 21 including providing a roller having a ply engaging surface forming ridges in engaged plies of said bead of material.
 28. The article formed in accordance with the method of claim
 28. 29. The method of claim 21 including providing a roller having a ply engaging surface provided with axially space circular grooves.
 30. The article formed in accordance with the method of claim
 29. 31. The method of claim 21 including providing a roller having a transversely curved ply engaging surface. 32, The article formed in accordance with the method of claim
 31. 33. The method of claim 21 including providing a substructure of said article in a diminished, approximate facsimile of an intended configuration of said object.
 34. The article formed in accordance with the method of claim
 33. 35. The method of claim 33 including machining the objected formed by the application of said material onto said substructure into a selected final configuration.
 36. The article formed in accordance with the method of claim
 35. 37. The method of claim 33 including applying said material on said substructure in a configuration exceeding said intended final configuration of said article, and removing a portion of said material exceeding said intended final configuration of said article.
 38. The article formed in accordance with the method of claim 37,
 39. The article of claim 34 wherein said substructure is formed of a group consisting of a plastic and a metal.
 40. The article of claim 34 wherein said substructure is formed in a lattice configuration. 